1. Application:
Used for fixing crane rail tracks at port and factories.
2. Size
No.62, No.114, No.103, No.106, No.120
3. Material
الفولاذ الطري
|
Chemical composition |
C |
Si |
Mn |
P |
S |
|
≤0.20% |
≤0.35% |
≤1.4% |
≤0.045% |
≤0.045% |
|
|
Mechanical properties |
Tensile strength |
Yield strength |
Hardness (HB) |
|
|
|
370-500MPa |
≥235MPa |
≥120 |
|
|
4. Manufacture method
Hot forging
5. Mark
Manufacture ID, Product ID
6. Coating
Plain, zinc plated, Hot dip galvanized.
7. Supply reference
1) USA
2) Chile
*أفريقيا
1. Application:
Used for fixing crane rail tracks at port and factories.
2. Size
KR type A, KR type B, KR type K
3. Material
Middle carbon steel
|
Chemical composition |
C |
Si |
Mn |
P |
S |
|
0.42-0.5% |
0.17-0.37% |
0.5-0.8% |
≤0.035% |
≤0.035% |
|
|
Mechanical properties |
Tensile strength |
Yield strength |
|
|
|
|
≥690MPa |
≥483MPa |
|
|
|
4. Manufacture method
Hot forging
5. Mark
Manufacture ID, Product ID
6. Coating
Plain, zinc plated, Hot dip galvanized.
*أوروبا
1. Application:
Used for fixing crane rail tracks at port and factories.
2. Size
M10, M12, M12 LA, M12 LAS
3. Material
Middle carbon steel
|
Chemical composition |
C |
Si |
Mn |
P |
S |
|
0.42-0.5% |
0.17-0.37% |
0.5-0.8% |
≤0.035% |
≤0.035% |
|
|
Mechanical properties |
Tensile strength |
Yield strength |
|
|
|
|
≥600MPa |
≥355MPa |
|
|
|
4. Manufacture method
Hot forging
5. Mark
Manufacture ID, manufacture month and year
6. Coating
Plain, zinc plated, Hot dip galvanized.
7. Supply reference
1) German